MAE 6234.5 Raw Material of Sintered Iron without Bore for Plain Bearing Production
Solid material of sintered steel similar SINT A10, to be machined into plain bearings. After machining, the work piece should be coated with lubricants. The stated values for outer diameter and length are the minimum. The parts may be delivered a bit larger.Surface pressure: max. 35 N/mm², dependent on speed and diameter. Temperature range: -20°C to +120°C.
| SKU | D [mm] | L [mm] | Weight [kg] |
|---|---|---|---|
| 6234.5-15-30 | 15 | 30 | 0,03 |
| 6234.5-20-25 | 20 | 25 | 0,05 |
| 6234.5-20-50 | 20 | 50 | 0,09 |
| 6234.5-25-25 | 25 | 25 | 0,07 |
| 6234.5-25-50 | 25 | 50 | 0,14 |
| 6234.5-32-40 | 32 | 40 | 0,19 |
| 6234.5-32-80 | 32 | 80 | 0,37 |
| 6234.5-42-50 | 42 | 50 | 0,40 |
| 6234.5-42-100 | 42 | 100 | 0,80 |
| 6234.5-45-90 | 45 | 90 | 0,83 |
| 6234.5-52-60 | 52 | 60 | 0,74 |
| 6234.5-52-120 | 52 | 120 | 1,48 |
| 6234.5-62-120 | 62 | 120 | 2,10 |
| 6234.5-70-120 | 70 | 120 | 2,68 |
| 6234.5-80-120 | 80 | 120 | 3,50 |